Nano/submicron Ag paste for low-temperature sintering

Nano/submicron Ag particles can be sintered at low temperatures. As pastes, they can be made into printed circuits at low temperatures. They are particularly suitable for printing on organic substrates, including PET film, which cannot be subjected to high temperatures.

极速赛车最快开奖

  • Composed of Ag particles of 120 nm average diameter, organic polymers and organic solvents.
  • By curing (100℃~250℃) under air, low-resistance sintered Ag layer can be formed (refer to the figure below).
  • Wires of less than 100 µm can be printed by screen-printing.
  • Printed wires are highly durable when bent.
    After a printed wire had been bent 100,000 times (bending radius R= 0.5mm), no change in resistance was observed.
    (*Bending durability varies greatly depending on the base material.)
  • Ag paste appearance

    Ag concentration: 70wt%
    Paste viscosity: 60−120 Pa・s (10S-1)
  • SEM image of Ag particles

    Ag particles average diameter: 120nm
  • Printed wire image

    Printing base material: PET film
  • Enlarged image of wiring